ABSTRACT
Many patients with large-area tooth defect need cast post-core crown restoration. However, the color defect of the cast post-core will affect the final restorative result, especially that of the anterior teeth. A new technology of color masking by applying CERAMAGE polymeric porcelain to the cast metal post-core surface improves the color of a full-ceramic restoration of anterior teeth and may provide a new alternative for the aesthetic repair of anterior teeth with a large area of defective tooth.
Subject(s)
Humans , Ceramics , Crowns , Dental Porcelain , Esthetics, Dental , Post and Core TechniqueABSTRACT
OBJECTIVES@#This study was performed to investigate the microstructure and mechanical properties of dental zirconia manufactured by digital light processing (DLP) 3D printing and the clinical application prospects of this material.@*METHODS@#The experiment (DLP) group was zirconia manufactured by DLP 3D printing, and the control (MILL) group was milled zirconia. The density, grain size, and phase composition were measured to study the microstructure. Flexural strength was measured by using three-point bending tests, while Vickers hardness was determined through a Vickers hardness tester. Fracture toughness was tested using the single-edge V-notched beam method.@*RESULTS@#Zirconia density of the DLP group was (6.019 8±0.021 3) g·cm@*CONCLUSIONS@#Zirconia manufactured by DLP 3D printing had microstructure and mechanical properties similar to those of the milled zirconia. Only the flexural strength and the Vickers hardness of the experimental zirconia were slightly lower than those of the milled zirconia. Therefore, DLP-manufactured zirconia has a promising future for clinical use.